Heat sealable packaging film comprising propylene polymer substrate and a surface layer blend of olefin copolymer or interpolymer

ABSTRACT

Multiple-layer, heat-sealable films are described comprising a substrate layer of polypropylene homopolymer or copolymer, or blends thereof with compatible polyolefins; and at least one heat-sealable surface layer of an interpolymer of propylene and two different higher alpha-olefins; a copolymer of butene-1 and a higher alpha-olefin or an interpolymer of ethylene, propylene and a higher olefin. The films are prepared by extrusion coating or coextrusion and can be oriented.

SUMMARY OF THE INVENTION

This invention relates to multi-layer films having a wide range of heat sealing temperatures. The films comprise a core or substrate of propylene homopolymer, a copolymer of propylene and another olefin or a blend of the foregoing with up to 40% by weight of a different compatible polyolefin, and a surface layer on one or both sides of the substrate. The different compatible polyolefin is preferably the same polyolefin blend which is used for the surface layer. The heat-sealable surface layer which is present on either one or both sides of the substrate is

(1) an interpolymer of 1-90 mole percent of propylene, 1-98 mole percent of an alpha-olefin having four or more carbon atoms and 1-98 mole percent of a different alpha-olefin having four or more carbon atoms;

(2) a copolymer of 50-97 mole percent of butene-1 and 3-50 mole percent of an alpha-olefin having more than four carbon atoms; or

(3) an interpolymer of 2-94 mole percent of ethylene, 1-93 mole percent of propylene, and 5-97 mole percent of an alpha olefin having four or more carbon atoms.

The films of this invention can be produced by coextrusion of the surface layer material and the substrate material followed by biaxial orientation. Alternatively, the substrate can be extruded alone, stretched in the machine direction, then extrusion coated with the surface layer material and finally stretched perpendicular to the machine direction.

DETAILED DESCRIPTION OF THE INVENTION

Oriented polypropylene film has become a useful and widely used packaging film because of its good moisture barrier properties, stiffness, high-strength, and good optical properties. For widest utility, it is desired that the films be capable of being heat sealed over a broad range of temperatures. One means to achieve heat-sealability has been the application of a heat-sealable coating to the surface. A separate coating operation following orientation, however, is quite costly.

An alternate and less costly method of achieving heat-sealability is the coextrusion of a surface layer on one or both surfaces of a substrate. The surface layer is selected so it melts at a lower temperature than the underlying substrate. Coextruded oriented films have been prepared in which the oriented polypropylene substrate or core is encased in skins comprised of ethylene/propylene copolymer, butene-1 homopolymer or butene-1/ethylene copolymer, for instance. Such films are described in U.S. Pat. No. 4,125,662.

Many of the prior art films exhibit high seal strengths, but because of the relatively high melting point of the surface layer, the temperature range over which usable heat seals are formed is narrow. A narrow sealing range severely limits the utility of a packaging film. It is therefore one of the objects of this invention to provide multi-layer films which can be sealed over a wide range of temperatures and which have other desirable properties.

Another object of this invention is the provision of multi-layered sealable films which can be prepared without separate coating operations.

Still another object of this invention is the provision of films which have one layer which is heat-sealable over a wide range to provide a high-strength seal over a substrate layer which is heat-sealable to itself to provide a weaker, but useful seal.

Methods of extrusion coating and coextrusion are well known in the art and are suitable for the production of the films of this invention. Advantageously, when extrusion coating is used, the substrate material is extruded alone, stretched in the machine direction, extrusion coated with the surface material and then stretched perpendicularly to the machine direction. When coextrusion is utilized, the film obtained by coextrusion of the substrate material and the surface material is biaxially oriented. In either case, each surface layer constitutes 1-10% by weight of the total film.

For many applications two-layer films comprising a relatively high melting substrate layer and an easily sealable surface layer are particularly desirable. For example, where the film is used in packaging machinery such as devices known in the art as "horizontal form and fill" machines it is not only unnecessary but disadvantageous to have a film with two low melting sealable surfaces. This is because the surface not intended for sealing necessarily comes into contact with heated areas, for example, heated platens, and if the surface layer not intended for primary sealing melts at too low a temperature sticking may occur resulting in machine malfunction. Sticking and its consequences is reduced with the two-layer films of this invention by virtue of the higher melting point of the substrate layer which can be selected for optimum properties.

In certain specific embodiments of this invention, the substrate film comprises a mixture of a homopolymer of propylene or a copolymer of propylene and a compatible polyolefin. The compatible polyolefin is preferably the same or similar polyolefin used for the surface layer. The result is a film in which the adhesion between the substrate layer and the surface layer or layers is excellent. An additional advantage of such a film having two-layers is that the surfaces of the substrate layer exhibit improved sealability to each other as well as to the surface layer. The heat sealability of the substrate layer surfaces to each other is of particular advantage in the production of bags with heat-sealed seams. While the seams forming the bag, as such, are made by heat sealing a surface layer to a surface layer, it is often desired that the substrate surface be sealable to itself. For example, this is desirable in the area of the "flaps" where a bag is made with a seal at the top, at the bottom and along the back. It is considered undesirable that the "flap" resulting from the seal at the back of the bag protrude from the surface of the bag. With the two-layer films of this invention containing a proportion of the surface layer polymer in the substrate layer it is possible to obtain a useful degree of sealability of the substrate layer to itself where the flap meets the top and bottom of the bag. The strength of this seal between substrate surfaces is not nearly as strong as the strength of the seal between the surface layers, but is sufficient to adhere the flap to the top and bottom edges of the bag.

The copolymers of propylene useful as the substrate in this invention generally comprise propylene and another olefin comonomer such as ethylene, butene or higher olefins. Typically up to about 20 mole percent of the comonomer is used. Where the comonomer is ethylene preferably up to 10 mole percent of the comonomer is present in the copolymer.

The invention is illustrated by the following examples.

EXAMPLE 1

A surface layer comprising an interpolymer of propylene (85 mole percent), 1-butene (10 mole percent), and 1-hexene (5 mole percent) is coextruded with polypropylene homopolymer to form a three layer sheet having a polypropylene core and an interpolymer layer as its outer surfaces. The three-layer film is solidified, heated to a temperature of 225°-295° F., stretched 5X in the machine direction, heated to a temperature of 300°-330° F., and stretched 8X in the transverse direction. The thickness of each surface layer is 0.025 mil and that of the total film is 1.0 mil.

EXAMPLE 2

A surface layer material comprising an interpolymer of propylene (80 mole percent), 1-butene (15 mole percent), and 1-octene (5 mole percent) is extrusion coated on a polypropylene homopolymer substrate. The polypropylene sheet is preformed by extrusion, is solidified, heated to a temperature of 265°-295° F., stretched 6X in the MD direction, and the extrusion coated on one surface with the above described surface layer material. The coated material is then stretched transversely 8X at a temperature of 300°-330° F. The thickness of the film is 1.25 mils and that of the surface layer is 0.02 mil.

EXAMPLE 3

The procedure of Example 2 is followed except that the substrate sheet is a mixture of 80% polypropylene and 20% of the surface layer material which is heated to a temperature of 225°-295° F. prior to machine direction orientation.

EXAMPLE 4

A surface layer material comprising a copolymer of 1-hexene (10 mole percent) and 1-butene (90 mole percent) is coextruded with polypropylene homopolymer to form a three-layer sheet having a polypropylene core and a layer of copolymer on each of its outer surfaces. The three-layer film is solidified, heated to a temperature of 225°-295° F., stretched 5X in the machine direction, heated to a temperature of 300°-330° F., and stretched 8X in the transverse direction. The thickness of each surface layer is 0.025 mil and that of the total film is 1.0 mil.

EXAMPLE 5

A surface layer material comprising a copolymer of 1-octene (15 mole percent) and 1-butene (85 mole percent) is extrusion coated on a polypropylene homopolymer substrate. The polypropylene sheet is preformed by extrusion, is solidified, heated to a temperature of 265°-295° F., stretched 6X in the MD direction, and extrusion coated on one surface with the above described surface layer material. The coated material is then stretched transversely 8X at a temperature of 300°-330° F. The thickness of the film is 1.25 mils and that of the surface layer is 0.02 mil.

EXAMPLE 6

The procedure of Example 5 is followed except that the substrate sheet is a mixture of 80% polypropylene and 20% of the surface layer material which is heated to a temperature of 225°-295° F. prior to machine direction orientation.

EXAMPLE 7

A surface layer material comprising an interpolymer of ethylene (4 mole percent), propylene (90 mole percent) and 1-butene (6 mole percent) is coextruded with polypropylene homopolymer to form a three-layer sheet having a polypropylene core and an interpolymer layer on each of its outer surfaces. The three-layer film is solidified, heated to a temperature of 225°-295° F., stretched 5X in the machine direction, heated to a temperature of 300°-330° F., and stretched 8X in the transverse direction. The thickness of each surface layer is 0.025 mil and that of the total film is 1.0 mil.

EXAMPLE 8

A surface layer material comprising an interpolymer of ethylene (3 mole percent), propylene (7 mole percent), and 1-butene (90 mole percent) is extrusion coated on a polypropylene homopolymer substrate. The polypropylene sheet is preformed by extrusion, is solidified, heated to a temperature of 265°-295° F., stretched 6X in the MD direction, and the extrusion coated on one surface with the above described surface layer material. The coated material is then stretched transversely 8X at a temperature of 300°-330° F. The thickness of the film is 1.25 mils and that of the surface layer is 0.02 mil.

EXAMPLE 9

The procedure of Example 8 is followed except that the substrate sheet is a mixture of 80% polypropylene and 20% of the surface layer material which is heated to a temperature of 225°-295° F. prior to machine direction orientation. 

I claim:
 1. A multiple-layer, heat-sealable film comprising:(a) a substrate layer consisting essentially of a homopolymer of polypropylene, a copolymer of polypropylene, or a blend of said homopolymer or copolymer containing up to 40% by weight of a different compatible polyolefin; and (b) on at least one of the surfaces of the substrate layer, a surface layer comprisingan interpolymer of 1-90 mole percent of propylene, 1-98 mole percent of an alpha-olefin having four or more carbon atoms, and 1-98 mole percent of a different alpha-olefin having four or more carbon atoms.
 2. The multiple-layer, heat-sealable film of claim 1 in which the substrate is polypropylene homopolymer.
 3. The multiple-layer heat-sealable film of claim 1 in which the substrate is polypropylene copolymer comprising propylene and up to 10 mole percent of ethylene.
 4. The multiple-layer, heat-sealable film of claim 1 in which the substrate is polypropylene copolymer comprising propylene and up to 20 mole percent of a higher alpha-olefin.
 5. The multiple-layer, heat-sealable film of claim 1 in which the substrate is a blend of polypropylene homopolymer or polypropylene copolymer, and said interpolymer and the surface layer comprises said interpolymer.
 6. The multiple-layer, heat-sealable film of claim 1 in which both surfaces of the substrate have a layer comprising said interpolymer.
 7. The multiple-layer, heat-sealable film of claim 1 in which only one surface of the substrate has a layer comprising said interpolymer.
 8. The multiple-layer, heat-sealable film of claim 1 in which only one surface of the substrate has a layer comprising said interpolymer, and the substrate is a blend of polypropylene homopolymer or polypropylene copolymer, and said interpolymer. 